Model: UH-2
Standards: DIN 50159-1, ASTM-A1038-05, JB/T 9377-2010
Description
This portable ultrasonic hardness tester is mainly used to test the metal Rockwell hardness, Vickers hardness, Brinell hardnss, it has no damage to the test objects, it’s the unique hardness tester which has no damage to the part.
Suitable objects
It’s suitable for fine grain material parts of any shape and size, including below:
Electroplated coatings, nitration layer, carburized layer, sheet metal, small parts, and other parts can’t be measured by normal portable hardness tester;
Parts need no damage and indentation on surface
Large parts, hard to known-down parts, irregular parts
Features
No damage to the objects-no visible indentation on surface
High accuracy
Rapid test
Stable performance
Wide test range
Thin parts testable
Irregular parts testable
Mass storage capacity
Wifi bluetooth printer
Usb interface available
Multi kinds of probe optional for different test requirements
Technical specifications
| Test range | HRC 20-70, HV 20-1740, HB 76-618 |
| Indicting accuracy | ±1.0 HRC(HRC in 55-70), ±3% HV/HB complies to DIN 50159-1 |
| Load | 10Nf±1Nf |
| Pressure head | 136°diamond |
| Data storage capacity | 999groups( 5data in each group) |
| Testable part min width | 1mm |
| Testable part min thickness | 1.5mm(5N probe) |
| Testable plating layer min thickness | 8um(chromeplated) |
| Continuous working timePower supply | 8hrs2000mah 7.4V rechargeable battery or 220V AC Power |
| Overall size | 178×84×36mm |
| Probe length | 150mm |
| Net weight | 400g |
| Ambient temperature | -10℃~50℃ |